Characteristics :
A heavy coated, hydrogen controlled, iron powder type electrode, suitable for welding of high tensile steels having tensile strength of 110,000 psi upwards.

Applications :
Suitable for welding of low alloy high tensile steels, Nickel steels, Ni-Moly steels, steels such as T-1, NA-XTRA, 70, HY100, Q2(N), boilers, pressure vessels, earthmoving equipment, heavy structures etc.

Typical Weldmetal Composition

 Element

Percent

C 0.06
Si 0.3
Mn 1.5
S 0.02
P 0.015
Ni 2.0
Cr 0.2
Mo 0.4

Typical Mechanical Properties of all weld Metal

Ultimate Tensile Strength Kg/mm2

Yield Strength Kg/mm2

Elongation % (L=5d)

CVN Impact Strength at +200C.Kgm

80 71 22 15

Classifications :

AWS A5.1 :

E 11018 M

Current Range & Packing Data :


Size MM DxL

Current Range (Amps) AC or DC (+)

Pieces per Packet

Pieces per Carton

6.30x450 250-330 30 120
5.00x450 200-240 45 180
4.00x450 140-190 80 320
3.15x450 100-140 110 440
2.50x350 60-90 160 640

Instructions:
  • Keep electrodes dry.
  • Rebake electrodes at 3500C. for one hour.
  • Do not use excessive current.
  • Hold short arc.
  • Use good fit-up on joints.
  • Adopt proper sequence.
  • Slow and uniform cooling is recommended.

HOME | WELDING ELECTRODES | TUNGSTENALUMINUMCO2 MIG WIRE  | SS TIG WIRE  |  FLUX CORED WIRE  |  SAW WIRE  |  AWS STANDARDS | ENQUIRY  | CONTACT US

 

Welding Electrodes & Wire Nashik, India

 

Copyright 2013. All rights reserved. All data is provided for informational purposes only.
Site Developed & Maintained By: C-Tech Solutions

site stats