Mild Steel High Efficiency Electrodes - Deepweld

Electrodes

Mild Steel High Efficiency Electrodes - Deepweld India

Mild Steel High Efficiency Electrodes

Nashik Mild Steel High Efficiency Electrodes - Deepweld

Deepweld

 

Mild Steel High Efficiency Electrodes - Deepweld

Characteristics :
A heavy coated, iron powder, deep penetration electrode for butt & fillet welds. Steels up to 14 mm thickness can be welded without edge preparation of bevelling. To achieve production targets electrodes can be used at higher current and faster speed.Deposition efficiency approx. 103%. Can be used only in flat and horizontal position. The deposited weldmetal is of Radiographic quality.

Applications :
Welding of Heavy structures, Bridges, Tanks, Shipdeck plates by deep penetration technique thus eliminating beveling anf refilling of the groove. Penetration beyond the root for depositing fillet weld.

Typical Weldmetal Composition

 Element

Percent

C 0.06-0.10
Mn 0.45-0.75
Si 0.40-0.65
P 0.03 Max
S 0.03 Max

Typical Mechanical Properties of all weld Metal

Ultimate Tensile Strength Kg/mm2

Yield Strength Kg/mm2

Elongation % (L=5d)

CVN Impact Strength at 0 OC.Kgm

46-55 37-46 26-28 7-9

Classifications :

AWS A5.1 :

E 6027

DIN 1913 :

E 4152 AR 11 105

BS 639 :

E 4152 AR

Current Range & Packing Data :


Size MM DxL

Current Range (Amps) AC or DC (-)

Pieces per Packet

Pieces per Case

5.00x350 250-300 40 160
4.00x350 180-250 40 160
3.15x350 150-180 105 420
 

HOME | WELDING ELECTRODES | TUNGSTENALUMINUMCO2 MIG WIRE  | SS TIG WIRE  |  FLUX CORED WIRE  |  SAW WIRE  |  AWS STANDARDS | ENQUIRY  | CONTACT US

 

Welding Electrodes & Wire Nashik, India

 

Copyright 2013. All rights reserved. All data is provided for informational purposes only.
Site Developed & Maintained By: C-Tech Solutions

site stats